SARAYBOND
- Техническа спецификация
- Цветове
- Най-новото постижение на SARAYGROOP е новият материал който е чудесна имитация на керамични плочи, като предлага и богата цветова гама.
|
Техническа спецификация
| Alloy: EN AW-3003 [Al Mn1 Cu] |
| Alloy Composition |
Si |
Fe |
Cu |
Mn |
Zn |
Al |
0.6 |
0.7 |
0.05-0.2 |
1.0-1.5 |
0.10 |
Kalan |
| Mechanical Properies of Aluminum |
| Tensile Strength (Rm): |
min 170MPa - max 210MPa |
| Yield Strength (Rq0,2): |
min 150MPa |
| Elongation min. % (A 50mm): |
2 |
| Bend Radius 180º - 90º |
2.5t - 1.5t |
| Hardness HBW : |
54 |
PVDF Coating Finish
|
| Hardness : |
ASTM D 3363-74 (NCAA II-12) |
| Flexibility T-Bend : |
ASTM D 4145-83 (NCAA II-19) |
| Adhesion : |
ASTM D 4145-87 (NCAA II-5) |
| Abrasion : |
ASTM D 968-81 (NCAA II-12) |
| Resistance to Mortar : |
AAMA 605,2-91. TEST#7.7.2 |
| Resistance to Detergent : |
ASTM D 2248-73 (ECCA T5) |
| Resistance to Acid Pollutants : |
ASTM D 1308-87
AAMA 605.2-90,
TEST#7.7.3.1 |
| Resistance to Alkali : |
ASTM D 1308-87 |
| Salt Fog : |
ASTM B 117-85 (NCAA II-2) |
| Humidity : |
ASTM D 2247-87 D-714-87 |
| Color Retention : |
ASTM D 2244-85 D-2244-89 |
| Chalk Resistance : |
ASTM D 659-86 D-4214-89 |
ASTM: American Society for Testing and Meterials
AAMA: American Architectural Manufacturers Association
NCAA: National Coil Coaters Association
ECCA: European Coil Coating Association |
| COMPOSITE PANEL SIZES |
| Thickness : |
4 mm |
| Width : |
1020mm, 1250mm, 1500mm |
| Standart / Maximum Length : |
3200mm / 6000mm |
| Weight : |
5.5 Kg/m2 |
| COMPOSITE PANEL DIMENSIONAL TOLERANCES |
| Thickness : |
"+/- 0.2mm" |
| Width : |
"- 0mm / + 2mm" |
| Length : |
"- / + 4mm" |
| Diagonal Difference : |
max.3mm |
| Linearity : |
"+/- 0.2mm" |
| |
|
| OTHER PROPERTIES |
| Thermal Conductivity : |
1.102 Kcal/m.hr.ºC |
| Deflection Temperature : |
24x10 -6ºC |
| Linear Expansion : |
120ºC |
| Tensile Strength : |
8.5 Kg/mm2 |
| Elongation : |
27 % |
| Bending Strength : |
1.344 Kg/cm2 |
| Adhesion Strength (min) : |
18 Kg/2,5cm |
| Bending Elastic Modulus : |
3,746 Kg/mm2 |
|
|
|
|